Kajian Pengaruh Rapat Arus pada Pelapisan Hard Chrome terhadap Kekerasan Permukaan Baja Karbon Rendah (ST 37)

Nurdin Nurdin, Ichsan Maulana, Yuniati Yuniati, Ismi Amalia

Abstract


Abstract

The hard chrome process is one of the most widely used metal finishing methods to avoid corrosion, besides that hard chrome can improve metal quality such as hardness. The Hard chrome process is carried out by varying the current density of 30 Amp/dm2, 30 Amp/dm2, 40 Amp /dm2 and 50 Amp/dm2 with a coating time of 40 minutes at a solution temperature of 50 ᵒC. After the hard chrome process, the surface hardness test was carried out using a microvickers indent with a loading of 25 g.f. The results showed that the layer thickness and hardness increased when the current strength increased. The highest hardness value occurred at a current of 4 amperes of 551.6 VHN and a layer thickness of 1.80 microns.


Keywords


hard chrome, metal finishing, current density, coating time, hardness test

Full Text:

PDF

References


DAFTAR PUSTAKA

Wahyudi Y., 2016. Analisa Perbandingan Pelapisan Galvanis Elektroplating Dengan Hot Dip Galvanizing Terhadap Ketahanan Korosi Dan Kekerasan Pada Baja. REM (Rekayasa Energi Manufaktur) Jurnal, Vol. 1, No. 1, pp. em v1i1. 173-em v171i171. 173.

Sandi A.P., E.G. Suka, and Y.I. Supriyatna, 2017. Pengaruh Waktu Elektroplating Terhadap Laju Korosi Baja Aisi 1020 Dalam Medium Korosif Nacl 3%. Jurnal Teori dan Aplikasi Fisika, Vol. 5, No. 2, pp. 205-212.

Ngatin A., et al. Elektroplating Flash Chrome Pada Baja Karbon Rendah. in Prosiding Seminar Nasional Kimia UNY. 2017.

Hendrawan A.B., 2018. Pengaruh Variasi Waktu Proses Electroplating Chrome Pada Plat Baja Karbon Rendah Terhadap Kekuatan Tarik. Nozzle: Journal Mechanical Engineering, Vol. 7, No. 2, pp. 5-8.

Hamdani H., et al., 2021. Pengaruh Pengelasan Dan Media Quenching Terhadap Kekuatan Tarik Dan Kekerasan Material Astm a 36. Jurnal Teknologi, Vol. 21, No. 2, pp. 65-69.

Sakti F.R. and U. Rumendi, 2016. Analisis Ketebalan, Ketahanan Korosi, Dan Daya Lekat Lapisan Hasil Proses Hardchrome Plating Pada Baja Karbon Rendah Sebelum Dan Sesudah Case Hardening.

Setyahandana B. and Y.E. Christianto, 2017. Pengaruh Hard Chrome Plating Pada Peningkatan Kekerasan Baja Komponen Kincir. Media Teknika, Vol. 12, No. 1,

Alphanoda A.F., 2017. Pengaruh Jarak Anoda-Katoda Dan Durasi Pelapisan Terhadap Laju Korosi Pada Hasil Electroplating Hard Chrome. Jurnal Teknologi Rekayasa, Vol. 1, No. 1, pp. 1-6.

Sukarjo H. and R.S. Pani, 2018. Pengaruh Variasi Kuat Arus Listrik Dan Waktu Electroplating Nickel-Chrome Terhadap Ketebalan Lapisan Pada Permukaan Baja Karbon Rendah. Jurnal Engine: Energi, Manufaktur, dan Material, Vol. 2, No. 1, pp. 18-25.

Nasution D.I. and A.M. Sakti, 2018. Pengaruh Jarak Anoda Katoda Dan Waktu Pencelupan Pada Proses Pelapisan Nikel–Krom Terhadap Ketebalan Dan Kekerasan Lapisan Permukaan Knalpot Sepeda Motor. Jurnal Teknik Mesin, Vol. 6, No. 1,

Koten A.M., D.G. Adoe, and J.U. Jasron, 2016. Pengaruh Variasi Tegangan Dan Waktu Terhadap Kekerasan Lapisan Nikel Dengan Metode Electroplating Pada Coran Aluminium Scrap. LONTAR Jurnal Teknik Mesin Undana (LJTMU), Vol. 3, No. 1, pp. 1-8.

DP A.S.D., I.D.K. Okariawan, and N.H. Sari, 2015. Pengaruh Variasi Kuat Arus Listrik Dan Waktu Proses Electroplating Terhadap Kekuatan Tarik, Kekerasan Dan Ketebalan Lapisan Pada Baja Karbon Rendah Dengan Krom. Dinamika Teknik Mesin, Vol. 5, No. 2,




DOI: http://dx.doi.org/10.30811/teknologi.v22i1.2902

Refbacks

  • There are currently no refbacks.


Copyright (c) 2022 nurdin nurdin, Ichsan Maulana, Yuniati Yuniati, Ismi Amalia

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

INDEXING AND ABSTRACTING BY:

     

Jurnal Teknologi - Politeknik Negeri Lhokseumawe is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License 

©2021 All rights reserved | E-ISSN: 2550-0961; P-ISSN:1412-1476