Pengaruh Variasi Temperatur Tempering terhadap Kekerasan Baja JIS SUP 9A pada Mata Pisau

Nanda Aulia Fadli, Adi Saputra Ismy, Irwin Syahri Cebro

Abstract


The effect of tempering temperature variations on the hardness of the blade has been carried out on SUP 9A leaf spring steel material. The tempering process was carried out at temperatures of 300°C, 400°C, and 500°C with a holding time of 15 minutes and cooled in free air. Specimens without heat treatment and tempering results were tested for hardness using the Rockwell hardness test method and microstructure analysis using an optical microscope. From the results of the study, it was found that the hardness value obtained on the raw material specimen without heat treatment obtained a hardness value of 60.50 HRC, while the tempering temperature variation obtained the hardness value on specimen B (tempering temperature 300°C) of 66.90 HRC, specimen C (tempering temperature 400°C) of 64.70 HRC, while specimen D (tempering temperature 500°C) obtained a hardness value of 65.80 HRC. From the results of the specimen hardness test, the hardness value after heating was higher than the hardness value without heating treatment. Microstructural analysis shows that the higher the given temperature, the larger the grain of the steel structure looks. Without heat treatment the microstructure of the specimen is an irregular black bainite. Meanwhile, by heat treatment, the microstructure of the specimen is irregular black martensite.

Keywords


tempering, temperature, blade, SUP 9A steel, hardness

Full Text:

PDF

References


Suarsana I., I. Santhiarsa, and D. Negara, 2018. Pengaruh Perlakuan Temperatur Dan Media Pendinginan Terhadap Sifat Ketangguhan Baja Aisi 3215. J. METTEK, Vol. 4, No. 1, p. 23.

Wijaya R.D., 2015. Study Eksperimental Keuletan Baja Karbon Rendah Setelah Dilakukan Perlakuan Panas Austempering. JURNAL TEKNIK MESIN, Vol. 3, No. 1,

Saefuloh I., et al., 2018. Pengaruh Proses Quenching Dan Tempering Terhadap Sifat Mekanik Dan Struktur Mikro Baja Karbon Rendah Dengan Paduan Laterit. FLYWHEEL: Jurnal Teknik Mesin Untirta, Vol. 1, No. 1, pp. 56-64.

Purnomo D.J., S. Jokosisworo, and U. Budiarto, 2019. Analisa Pengaruh Holding Time Tempering Terhadap Kekerasan, Keuletan, Ketangguhan Dan Struktur Mikro Pada Baja St 70. Jurnal Teknik Perkapalan, Vol. 7, No. 1,

Rifnaldy R. and M. Mulianti, 2019. Pengaruh Perlakuan Panas Hardening Dan Tempering Terhadap Kekerasan (Hardness) Baja Aisi 1045. Ranah Research: Journal of Multidisciplinary Research and Development, Vol. 1, No. 4, pp. 950-959.

Halimi A.D., 2017. Uji Eksperimen Tingkat Kekerasan Dan Ketangguhan Baja Pegas Jis Sup 9 Dengan Metode Laku Panas Hardening Dan Tempering. Jurnal Teknik Mesin, Vol. 5, No. 03,

Asmadi A., S.Z. Nuryanti, and A. Nawawi, 2019. Austempering Dengan Pendingin Oli Pada Baja Strip Jis G4801 Sup 9. TEKNIKA: Jurnal Teknik, Vol. 6, No. 1, pp. 47-57.

Nurlina N., 2019. Pengaruh Pengujian Hardening Pada Baja Karbon Rendah Sebagai Solusi Peningkatan Kualitas Material. Jurnal Qua Teknika, Vol. 9, No. 1, pp. 11-20.

Hadi S. Pengaruh Komposisi Dan Struktur Mikro Terhadap Kekerasan Baja Karbon Dan Besi Cor. in Seminar Nasional Teknologi Terapan (MESIN). 2019.

Handbook A., 1996. Iron and Steel, Vol. 1. Metals Park, Ohio,

Nugroho F., 2017. Studi Komparasi Pengaruh Variasi Arus Pengelasan Terhadap Kekuatan Impak, Kekerasan, Dan Struktur Mikro Sambungan Las Pegas Daun Baja Sup 9 Pada Proses Las Smaw. Angkasa, Vol. 9, No. 2, pp. 57-66.

Affandi M., M. Ari, and D. Anggara. Analisa Pengaruh Waktu Penahanan Pada Proses Quenching–Partitioning Terhadap Sifat Mekanik Dan Struktur Mikro Baja Jis Sup 9a. in Proceedings Conference on Design Manufacture Engineering and its Application. 2017.




DOI: http://dx.doi.org/10.30811/teknologi.v22i1.2891

Refbacks

  • There are currently no refbacks.


Copyright (c) 2022 Nanda Aulia Fadli, Adi Saputra Ismy, Irwin Syahri Cebro

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

INDEXING AND ABSTRACTING BY:

     

Jurnal Teknologi - Politeknik Negeri Lhokseumawe is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License 

©2021 All rights reserved | E-ISSN: 2550-0961; P-ISSN:1412-1476