Penggunaan Amilum sebagai Pelapis Anti Korosi pada Baja Karbon dalam Lingkungan Asam Klorida 0,5 M

Muhammad Salahuddin, Irwan Irwan, Cut Aja Rahmawati

Abstract


The purpose of this paper was to determine the affect of amylum concentration and immersion time on the corrosion rate. Amylum is used as an anticorrosive coating on carbon steel in 0,5 M hydrochloric acid  environment. Amylum concentration and immersion time affect the corrosion rate. The longer immersion time, the corrosion rate increases while the higher the concentration, the corrosion rate decreases. The highest corrosion rate was obtained at 3.58 mpy while the lowest corrosion rate was 1.24 mpy, Corrosion rates in metals can be prevented by the coating method

Keywords


amylum, carbon steel, coating corrosion, corrosion rate

Full Text:

PDF

References


Taqwa M.L., I. Irwan, and P. Pardi, 2021. Penggunaan Ekstrak Daun Pepaya Sebagai Inhibitor Korosi Baja Karbon Dalam Lingkungan Crude Oil. Jurnal Teknologi, Vol. 21, No. 1, pp. 6-11.

Septianingsih D., E.G. Suka, and S. Suprihatin, 2014. Pengaruh Variasi Konsentrasi Asam Klorida Terhadap Laju Korosi Baja Karbon Rendah Astm a 139 Tanpa Dan Dengan Inhibitor Kalium Kromat 0, 2%. Jurnal Teori dan Aplikasi Fisika, Vol. 2, No. 2,

Stiadi Y., et al., 2019. Inhibisi Korosi Baja Ringan Menggunakan Bahan Alami Dalam Medium Asam Klorida. Jurnal Riset Kimia, Vol. 10, No. 1, pp. 51-65.

Ali F., D. Saputri, and R.F. Nugroho, 2014. Pengaruh Waktu Perendaman Dan Konsentrasi Ekstrak Daun Jambu Biji (Psidium Guajava, Linn) Sebagai Inhibitor Terhadap Laju Korosi Baja Ss 304 Dalam Larutan Garam Dan Asam. Jurnal Teknik Kimia, Vol. 20, No. 1,

Setiawan A., 2018. Sintesis Dan Karakterisasi Zno Sebagai Coating Antikorosi Zno/Al (Oh) 3 Pada Material Baja Karbon. Jurnal Teknik, Vol. 39, No. 1, pp. 55-61.

Erna M., et al., 2017. Efektifitas Kitosan Sebagai Pelapis (Coating) Korosi Pada Logam Zn, Fe, Al Dalam Media Hcl Dan H2so4. EduChemia (Jurnal Kimia dan Pendidikan), Vol. 2, No. 2, pp. 119-129.

Widawardhana D.K., Analisis Polyurethane Coating Pada Pelapisan Material Baja Astm A36 Dengan Beberapa Media Korosi. 2017, Institut Teknologi Sepuluh Nopember.

Anwar M.J. and E. Widodo, 2018. Karakterisasi Laju Korosi Baja St 40 Berlapis Polyester Putty Dalam Lingkungan Air Payau. REM (Rekayasa Energi Manufaktur) Jurnal, Vol. 2, No. 2, pp. 69-76.

Purba R., 2020. Pengaruh Laju Korosi Akibat Penambahan Kitosan Sebagai Pelapis (Coating) Korosi Terhadap Baja Karbon Rendah Dengan Media Hcl Dan Belimbing Wuluh Sebagai Pengganti H_2 [So] _4 Dengan Variasi Waktu.

Olajire A.A., 2018. Recent Advances on Organic Coating System Technologies for Corrosion Protection of Offshore Metallic Structures. Journal of Molecular Liquids, Vol. 269, pp. 572-606.

Afandi Y.K., I.S. Arief, and A. Amiadji, 2015. Analisa Laju Korosi Pada Pelat Baja Karbon Dengan Variasi Ketebalan Coating. Jurnal Teknik ITS, Vol. 4, No. 1, pp. G1-G5.

Ronasia D.A., Karakterisasi Amilum Dari Ubi Jalar (Ipomoea Batatas L.) Berwarna Kuning Dan Ungu. 2016, Fakultas Matematika Dan Ilmu Pengetahuan Alam (UNISBA).

Pramesti H.A., K. Siadi, and E. Cahyono, 2015. Analisis Rasio Kadar Amilosa/Amilopektin Dalam Amilum Dari Beberapa Jenis Umbi. Indonesian Journal of Chemical Science, Vol. 4, No. 1,

Sari M.G., et al., 2018. Epoxy/Starch-Modified Nano-Zinc Oxide Transparent Nanocomposite Coatings: A Showcase of Superior Curing Behavior. Progress in Organic Coatings, Vol. 115, pp. 143-150.




DOI: http://dx.doi.org/10.30811/teknologi.v22i1.2876

Refbacks

  • There are currently no refbacks.


Copyright (c) 2022 Muhammad Salahuddin, Irwan M.T., Cut Aja Rahmawati

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

INDEXING AND ABSTRACTING BY:

     

Jurnal Teknologi - Politeknik Negeri Lhokseumawe is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License 

©2021 All rights reserved | E-ISSN: 2550-0961; P-ISSN:1412-1476