Comparative study of performance of temiki (Melastomacandidum) and rubek (Calotropis gigantea) extract inhibitors for carbon steel in corrosive media
Abstract
The use of synthetic inhibitors that negatively affect the environment is still used. Organic inhibitors are the best and most environmentally friendly solutions such as Temiki plants (MelastomaCandidum) and Rubik (Calotropis Giganteen) which have good corrosion cell inhibitor properties and have the potential to be used as corrosion inhibitors. This study analyzed Temiki and Rubik extracts as corrosion inhibitors in carbon steel using the weight loss method in 3.5% NaCl solution and analyzed the efficiency of the inhibitors. Temiki and Rubik's are extracted by drying the leaves, stems and flowers under the sun. Then the material is mashed together and distilled by the solid-liquid method with the Soxhlet tool. Identification of plant components using Gas Chromatography-Mass Spectrometry (GC-MS). Density and viscosity were analyzed following ASTM D 4052 and ASTM D 445 standards. Weight loss method testing was carried out at inhibitor concentrations of 200, 300, 400 and 500 ppm, with soaking time for 15 weeks and data collection was carried out every week. The results of the analysis showed the highest corrosion rate in Temiki extract with a concentration of 500 ppm reaching 1,569 mpy and the lowest at a concentration of 500 ppm reaching 0.157 mpy. In Rubik's extract inhibitors, the highest corrosion rate occurred in 500 ppm inhibitors reaching 1,268 mpy, while the lowest occurred at 200 ppm concentrations reaching 0.331 mpy. The highest efficiency value is the 400 ppm Temiki inhibitor with efficiency reaching 82.89% and the lowest at 500 ppm reaching 19.55%. while for the efficiency of Rubik's extract inhibitors, the highest value was 62.71%, at a concentration of 200 ppm. While the lowest is 28.40%, at 500 ppm inhibitors. These results show that Temiki and Rubik's extracts can still function well as corrosion inhibitors in low-carbon steels in NaCl solution.
Keywords
Full Text:
PDFReferences
S. Winnik, Corrosion-Under-Insulation (CUI) Guidelines. Elsevier, 2016. doi: 10.1016/C2015-0-01794-4.
M. Ridha, S. Fonna, S. Huzni, J. Supardi, and A. K. Ariffin, “Atmospheric Corrosion of Structural Steels Exposed in the 2004 Tsunami-Affected Areas of Aceh,†Int. J. Automot. Mech. Eng., vol. 7, pp. 1014–1022, Jun. 2013, doi: 10.15282/ijame.7.2012.17.0082.
X. Hou, L. Gao, Z. Cui, and J. Yin, “Corrosion and Protection of Metal in the Seawater Desalination,†IOP Conf. Ser. Earth Environ. Sci., vol. 108, p. 022037, Jan. 2018, doi: 10.1088/1755-1315/108/2/022037.
P. Lakkanasri and G. Lothongkum, “Effect of monoethanolamine on corrosion of A283 carbon steel in Propionic acid solution,†Eng. J., vol. 23, no. 4, pp. 183–191, 2019, doi: 10.4186/ej.2019.23.4.183.
O. A. F, “Corrosion Inhibition of AISI/SAE Steel in a Marine Environment,†Leonardo J. Sci. 47-52.
D. R. Gusti, F. Farid, and I. Lestari, “Ekstrak Kulit Kayu Akasia Sebagai Inhibitor pada Laju Korosi Baja,†Ratnasari, pp. 31–36, 2013.
J. Halambek, A. Žutinić, and K. Berković, “Ocimum basilicum L. oil as corrosion inhibitor for aluminium in hydrochloric acid solution,†Int. J. Electrochem. Sci., vol. 8, no. 9, pp. 11201–11214, 2013.
N. Y. P. P. Vivia Widyati, Ismi Hidaya, “PEMANFAATAN EKSTRAK METANOL DAUN TUMBUHAN ASHITABA ( Angelica keiskei ) SEBAGAI INHIBITOR KOROSI BAJA,†pp. 934–946, 2018.
E. Elqars et al., “Expired Chicken Egg-White Extract’s Adsorption Behavior As a Corrosion Inhibitor for Carbon Steel in 1M HCl,†J. Chem., vol. 2021, 2021, doi: 10.1155/2021/3416092.
O. K. Abiola and A. O. James, “The effects of Aloe vera extract on corrosion and kinetics of corrosion process of zinc in HCl solution,†Corros. Sci., vol. 52, no. 2, pp. 661–664, 2010, doi: 10.1016/j.corsci.2009.10.026.
Y. Pratesa, A. Purnawidhi, and N. Rahwinarni, “Studi Pemanfaatan Estrak Daun Pegagan untuk Inhibitor Korosi Ramah Lingkungan untuk Material API 5CT J55 di Lingkungan Air Formasi,†J. Tek. Mesin, vol. 7, no. 1, p. 5, Mar. 2018, doi: 10.22441/jtm.v6i4.2178.
D. B. Left, M. Zertoubi, S. Khoudali, and M. Azzi, “New Application of Chamaerops Humilis L . Extract as a Green Corrosion Inhibitor for Reinforcement Steel in a Simulated Carbonated Concrete Pore Solution,†vol. 36, no. 4, pp. 249–257, 2018, doi: 10.4152/pea.201804249.
J. Backer, C.A. and Bakhuizen V.d. Brink, “Flora of Java Volume 3,†Netherlands Organ. Adv. Res., vol. volume 3, 1968.
S. S. Kumar, “Evaluation of Anti Microbial Activity and Phytochemical analysis of Organic Solvent extracts of Calotropis gigantea,†IOSR J. Pharm., vol. 2, no. 3, pp. 389–394, Jan. 2012, doi: 10.9790/3013-0230389394.
M. R. Habib and M. R. Karim, “Antimicrobial and Cytotoxic Activity of Di-(2-ethylhexyl) Phthalate and Anhydrosophoradiol-3-acetate Isolated from Calotropis gigantea (Linn.) Flower,†Mycobiology, vol. 37, no. 1, p. 31, 2009, doi: 10.4489/MYCO.2009.37.1.031.
R. Dhivya and K. Manimegalai, “Preliminary Phytochemical Screening and GC- MS Profiling of Ethanolic Flower Extract of Calotropis,†J. Pharmacogn. Phytochem., vol. 2, no. 3, pp. 28–32, 2013.
V. Vadlapudi, M. Behara, D. S. V. G. K. Kaladhar, S. V. N. Suresh Kumar, B. Seshagiri, and M. John Paul, “Antimicrobial profile of crude extracts Calotropis procera and Centella asiatica against some important pathogens,†Indian J. Sci. Technol., vol. 5, no. 8, pp. 3132–3136, 2012, doi: 10.17485/ijst/2012/v5i8.25.
K. S. and L. L. Starr, F., “Melastoma candidum Asian Melastome Melastomataceae,†Maui, Hawai’i., 2003.
ASTM. International (2004) ASTM G31-72, “Standard Practice for Laboratory Immersion Corrosin Testing of Metals,†United State.
ASTMG1-03, “Standard Practice for Preparing , Cleaning , and Evaluating Corrosion Test,†pp. 1–9.
T. et Al., “Phytochemical Screening And Extraction: A Review,†Int. Pharm. Sci., vol. 1, pp. 98-106., 2011.
P. Siagian, R. A. M. Napitupulu, E. Y. Setyawan, and M. F. Amadika, “Optimization of Nickel Electroplating on Low Carbon Steel for Corrosion Resistance using Immersion Corrosion test with 3.5% NaCl,†Polimesin, vol. 21, no. 1, pp. 46–49, 2023.
D. Jones, Principles and Prevention of Corrosion. New York: Macmillan Publishing Company, 1992.
A. A. Alamiery, “Investigations on corrosion inhibitory effect of newly quinoline derivative on mild steel in hcl solution complemented with antibacterial studies,†Biointerface Res. Appl. Chem., vol. 12, no. 2, pp. 1561–1568, 2022, doi: 10.33263/BRIAC122.15611568.
F. M. Mahgoub, A. M. Hefnawy, and E. H. Abd Alrazzaq, “Corrosion inhibition of mild steel in acidic solution by leaves and stem extract of acacia nilotica,†Desalin. Water Treat., vol. 169, pp. 49–58, 2019, doi: 10.5004/dwt.2019.24681.
ASTM D445-06, “Standard Test Method for Kinematic Viscosity of Transparent and Opaque Liquids (and Calculation of Dynamic Viscosity).,†Man. Hydrocarb. Anal. 6th Ed., pp. 1–10, 2008.
The United States of America, “ASTM D4052 : Standard test method for density adn relatrive density of liquids by digital density meter,†An am, pp. 688–691, 1995.
V. Pourzarghan and B. Fazeli-Nasab, “The use of Robinia pseudoacacia L fruit extract as a green corrosion inhibitor in the protection of copper-based objects,†Herit. Sci., vol. 9, no. 1, pp. 1–14, 2021, doi: 10.1186/s40494-021-00545-w.
N. Subekti, J. W. Soedarsono, R. Riastuti, and F. D. Sianipar, “Development of environmental friendly corrosion inhibitor from the extract of areca flower for mild steel in acidic media,†Eastern-European J. Enterp. Technol., vol. 2, no. 6–104, pp. 34–45, 2020, doi: 10.15587/1729-4061.2020.197875.
J. Zhang, Z., Dong, C., Sun, X., & Liu, “Corrosion inhibition of carbon steel in acidic medium by 5-hydroxymethylfurfural,†Appl. Surf. Sci., vol. 407, pp. 432–439, 2017.
M. Zhu et al., “Corrosion inhibition of eco-friendly nitrogen-doped carbon dots for carbon steel in acidic media: Performance and mechanism investigation,†J. Mol. Liq., vol. 342, p. 117583, Nov. 2021, doi: 10.1016/j.molliq.2021.117583.
F. Menegazzo, E. Ghedini, and M. Signoretto, “5-Hydroxymethylfurfural (HMF) production from real biomasses,†Molecules, vol. 23, no. 9, pp. 1–18, 2018, doi: 10.3390/molecules23092201.
I. A. Idris, A. U. Bello, and B. Usman, “Experimental and Theoretical Evaluation Of Corrosion Inhibition of Honeycomb Propolis Extract On Mild Steel In Acidic Media,†J. Mater. Environ. Sci, vol. 2022, no. 5, p. 5, 2022, [Online]. Available: http://www.jmaterenvironsci.com
A. S. Obot, E. J. Boekom, B. N. Ita, and E. C. Utam, “Kinetics Consideration of Ethanol Leaves Extract of Costus Lucanusianus As Green Corrosion Inhibitor for Mild Steel and Aluminium in Hcl Solution,†Int. J. Res. -GRANTHAALAYAH, vol. 10, no. 1, 2022, doi: 10.29121/granthaalayah.v10.i1.2022.4461.
N. Bhardwaj, P. Sharma, and V. Kumar, “Oryza sativa plant extract in 15% hydrochloric acid as a green corrosion inhibitor on the surface of stainless steel 410,†Tenside, Surfactants, Deterg., vol. 59, no. 1, pp. 81–94, 2022, doi: 10.1515/tsd-2021-2355.
V. Vorobyova, O. Sikorsky, M. Skiba, and G. Vasyliev, “Quebracho tannin as corrosion inhibitor in neutral media and novel rust conversion agent for enhanced corrosion protection,†South African J. Chem. Eng., vol. 44, no. December 2022, pp. 68–80, 2023, doi: 10.1016/j.sajce.2023.01.003.
S. Mashooque, M. Kumar, and I. N. Unar, “Effect of Aloe Vera Extract as Green Corrosion Inhibitor on Medium Carbon Steel in SulphuricAcid Environment,†Pakistan J. Anal. Environ. Chem., vol. 23, no. 1, pp. 70–78, 2022, doi: 10.21743/pjaec/2022.01.07.
M. A. Omran, M. Fawzy, A. E. D. Mahmoud, and O. A. Abdullatef, “Optimization of mild steel corrosion inhibition by water hyacinth and common reed extracts in acid media using factorial experimental design,†Green Chem. Lett. Rev., vol. 15, no. 1, pp. 214–230, 2022, doi: 10.1080/17518253.2022.2032844.
A. A. Rosyadi, F. Gustiawan, M. Darsin, Y. Hermawan, and M. Asrofi, “Jurnal Polimesin,†Polimesin, vol. 20, no. 2, pp. 121–127, 2022.
M. Şahin, S. Bilgiç, and G. Gece, “Inhibition of armco iron corrosion in 1 m hcl medium using saponin: Experimental and computational studies,†Int. J. Corros. Scale Inhib., vol. 9, no. 4, pp. 1444–1458, 2020, doi: 10.17675/2305-6894-2020-9-4-16.
T. Sithuba et al., “Corrosion inhibitory potential of selected flavonoid derivatives: Electrochemical, molecular⋅⋅⋅Zn surface interactions and quantum chemical approaches,†Results Eng., vol. 16, no. October, p. 100694, 2022, doi: 10.1016/j.rineng.2022.100694.
M. Wahyuni, D. Djamas, and Ratnawulan, “Pegaruh waktu perendaman baja dengan ekstrak buah pinang dan HCl terhadap laju korosi dan potensial logam,†Pillar of Phisics, vol. 2, pp. 59–67, 2013.
A. Zouitini et al, “Corrosion inhibition behavior of quinoxaline derivative as a green corrosion inhibitor for mild steel in hydrochloric acid: Electrochemical, weight loss and DFT simulations studies,†Moroccan J. Chem, vol. 6, pp. 391–403, 2018.
A. Chaouiki, M. Chafiq, A. H. Al-Moubaraki, M. Bakhouch, M. El Yazidi, and Y. G. Ko, “Electrochemical behavior and interfacial bonding mechanism of new synthesized carbocyclic inhibitor for exceptional corrosion resistance of steel alloy: DFTB, MD and experimental approaches,†Arab. J. Chem., vol. 15, no. 12, p. 104323, Dec. 2022, doi: 10.1016/j.arabjc.2022.104323.
S. Kumar, R. Singh, N. S. Maurya, and R. Vikram, “Monitoring of Corrosion in the Pipeline of a Distribution Network Using Weight Loss Method and Image Processing Technique,†J. Mater. Eng. Perform., Dec. 2022, doi: 10.1007/s11665-022-07750-z.
K. K. Anupama, K. M. Shainy, and A. Joseph, “Excellent Anticorrosion Behavior of Ruta Graveolens Extract (RGE) for Mild Steel in Hydrochloric Acid: Electro Analytical Studies on the Effect of Time, Temperature, and Inhibitor Concentration,†J. Bio- Tribo-Corrosion, vol. 2, no. 1, p. 2, Mar. 2016, doi: 10.1007/s40735-016-0032-5.
T. Laabaissi et al., “New quinoxaline derivative as a green corrosion inhibitor for mild steel in mild acidic medium: Electrochemical and theoretical studies,†Int. J. Corros. Scale Inhib., vol. 8, no. 2, pp. 241–256, 2019, doi: 10.17675/2305-6894-2019-8-2-6.
N. J. N. Nnaji, C. O. B. Okoye, N. O. Obi-Egbedi, M. A. Ezeokonkwo, and J. U. Ani, “Spectroscopic Characterization of Red Onion Skin Tannin and It’s use as Alternative Aluminium Corrosion Inhibitor in Hydrochloric Acid Solutions,†Int. J. Electrochem. Sci., vol. 8, no. 2, pp. 1735–1758, Feb. 2013, doi: 10.1016/S1452-3981(23)14261-1.
DOI: http://dx.doi.org/10.30811/jpl.v21i6.4577
Refbacks
- There are currently no refbacks.
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional .
Alamat Surat :
Politeknik Negeri LhokseumaweJl. Banda Aceh-Medan Km 280
Buketrata, Lhokseumawe, 24301, Aceh, Indonesia