Corrosion Rate Analysis on SA 240 TP 904L Material Experience Multiple Repair

Muhammad Ari; Dika Anggara; Amar Sastra Adi

doi:10.30811/jowt.v5i1.4019

Corrosion Rate Analysis on SA 240 TP 904L Material Experience Multiple Repair

Muhammad Ari, Dika Anggara, Amar Sastra Adi

Abstract

Weld imperfections are likely to arise during any welding process. Due to the enormous number of joints that could result in weld defects, welding process faults could happen. Repair procedures are required to address welding defects. Multiple repairs are required if welding mistakes are made repeatedly. The duplex material used in this study is SA 240 TP 904L. By altering the repair procedure treatment 1x, 3x, 5x, and without repair, the welding process is carried out utilizing the SMAW method and E309L filler. Microstructure testing, ferrite content testing, and 3-electrode cell corrosion are the test techniques used. The relationship between the corrosion rate and the amount of ferrite content was deduced from the test data. The corrosion rate increases as the ferrite content rises due to several repairs.

Keywords

corrosion rate, defect, multiple repairs, duplex.

Full Text:

PDF

References

Iman Agha Ali, "The effect of repeated repair welding on mechanical and corrosion properties of stainless steel 316L," Materials & Design, vol. 54, pp. 331-341, February 2014.

Zeeshan Ahmad, "Effect of multiple repair welding on mechanical performance and corrosion resistance of quenched and tempered 30CrMnSiA steel," Journal of the Brazilian Society of Mechanical Sciences and Engineering , vol. 39, p. 1233–1243, 2017.

J. Kristin R. Carpenter, "The effects of multiple repair welds on a quenched and tempered steel for naval vessels," Welding in the World , vol. 65, 2021.

P. W. Bimantoro, "Pengaruh Multiple Repair Welding pada Pengelasan GTAW dan Smaw Terhadap Struktur Mikro, Ferrite Number, Sifat Mekanik dan Laju Korosi pada Material," Surabaya, 2016.

B. Holmes, M. Gittos, M. Dodge and K. Sotoudeh, "Ferrite Measurement in Duplex Stainless Steels," in CORROSION 2019, Nashville, Tennessee, USA, March 24 2019.

"Langley Alloys," 2023. [Online]. Available: https://www.langleyalloys.com/knowledge-advice/what-is-ferrite-content-in-duplex-stainless-steel/. [Accessed June 2023].

ASME Sect. II A Material, 2015.

ASME Sect. II C Specifications for Welding Rods, Electrodes, and Filler Metals, 2015.

A. G5, "Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements," 1999.

A. S. Adi, " Analisis Multiple Repair Pada Pengelasan Material SA 240 TP 904l Terhadap Struktur Mikro, Ferrite Content, Kekerasan, dan Laju Korosi," Surabaya, 2018.

DOI: http://dx.doi.org/10.30811/jowt.v5i1.4019