Pengaruh masukan panas terhadap struktur mikro dan sifat mekanik sambungan pipa 5L X65 dengan proses pengelasan kombinasi STT SMAW

Muhamad Iqbal Farhani; M Thoriq Wahyudi; Mochammad Karim Al Amin

doi:10.30811/jowt.v2i2.2062

Pengaruh masukan panas terhadap struktur mikro dan sifat mekanik sambungan pipa 5L X65 dengan proses pengelasan kombinasi STT SMAW

Muhamad Iqbal Farhani, M Thoriq Wahyudi, Mochammad Karim Al Amin

Abstract

Welding with the STT (Surface Tension Transfer) process is the latest innovation from the GTAW (Gas Tungsten Arc Welding) welding process, where STT is commonly used in the open root while the research carried out is the layer at the root and hot pass because it was chosen for the welding process with low heat input. . The research objective was to determine the effect of heat input or heat input of combination welding STT compared to GTAW on macro macro structure and mechanical properties of 5L X65 pipe welding joints. The results of this study compare the STT welding process with GTAW. Testing of the two processes will be assessed from the results of their mechanical properties through tensile and hardness, micro-macro structure and SEM. From the microstructure test and SEM, there is a not too significant effect on the differences in grain shape and content of ferrite acicular and ferrite widmanstatten, especially in the weldmetal area and grain changes in the HAZ area. From the hardness test, the comparison of the results of STT-SMAW, the hardness value is higher but not too significant than the GTAW-SMAW results due to the influence of heat input. The results from the tensile obtained that the STT-SMAW value has higher tensile strength and yield but not too significant compared to GTAW-SMAW, and all welding results still have values that fall into the standard range

Keywords

Surface Tension Transfer, Tensile, Hardness, Heat Input, Microstructure

Full Text:

PDF

References

S. Widarto, Teknologi Pengelasan Logam. Jakarta: Gagas Media. 2007

R. Alagesan and T. S. Kumar, “Optimization of welding cycle time by establishing full GMAW process (STT and P-GMAW) through a newly designed semi-automatic welding positioner,” Int J Res Eng Technol, vol. 3, 2014.

P. Adi, H. Ismar, and T. Petar, “Advantages of MAG-STT welding process for root pass welding in the oil and gas industry,” TEM J., vol. 5, no. 1, p. 76, 2016.

N. Milosevic, K. Marije, B. Serbia, O. Popovic, and R. P. Cvetkovic, “SURFACE TENSION TRANSFER (STT) WELDING.”

S. Radića and N. Travnik, “MONITORING OF MAIN WELDING PARAMETERS AT STT WELDING PROCESS.”

B. Despotović, I. Samardžić, T. Marsenić, B. Brechelmacher: Some aspects of STT welding process application in steam boiler manufacturing, 3rd International conference Mechanization, automation and robotization in welding and allied processes, Zadar, Croatia, 2005

H. Hamdani, “Pengaruh Masukan Panas Proses Pengelasan terhadap Sifat Mekanik Baja AISI 1045 suatu Kajian Analitis dan Analisa Numerik,” J. Polimesin, vol. 17, no. 1, pp. 1–8.

H. Hamdani, A. Ibrahim, and S. Sariyusda, “PENGARUH MASUKAN PANAS PROSES PENGELASAN TERHADAP SIFAT MEKANIK BAJA AISI 1045,” Mek. J. Ilm. Tek. Mesin, vol. 1, no. 2, 2015.

S. Mizhar and I. H. Pandiangan, “Pengaruh Masukan Panas Terhadap Struktur Mikro, Kekerasan Dan Ketangguhan Pada Pengelasan Shield Metal Arc Welding (SMAW) Dari Pipa Baja Diameter 2, 5 Inchi,” J. Din., vol. 2, no. 14, 2014.

Y. NUGROHO and D. Bayuseno, “ANALISIS KEGAGALAN LAS DAN REKOMENDASI STANDARD OPERATING PROCEDURE (SOP) PADA PENGELASAN PIPA KONDENSOR PT. SIEMENS INDONESIA.” Mechanical Engineering Departement, Faculty Engineering of Diponegoro University, 2012.

ASME SectionIX. Welding, Brazing and Fusing Qualification. New York:

THE AMERICAN SOCIETY OF MECHANICAL ENGINEERING. 2015.

DOI: http://dx.doi.org/10.30811/jowt.v2i2.2062