Kinerja pahat karbida berlapis titanium Aluminium Nitrida (TiAlN) pada pembubutan kering baja ASTM A 29 grade 1038
Abstract
The use of coated carbide-based cutting tools (WC + Co) dominates in the metal cutting industry. From the results of previous studies that layered carbide chisels have better toughness when compared to carbide chisels that are not coated with a coating material. The coating material is very influential in the performance of cutting tools which during the cutting process takes place the coating material can function as a solid lubricant that can reduce the cutting temperature. The purpose of this study was to determine the age of using Titanium Aluminum Nitride (TiAlN) carbide chisels with DCGX T3 1105-AL type by varying the cutting speed (Vc) of 70, 110, and 250 m / min, while feed motion (f) = 0, 1 mm / rotation and cutting depth (a) 1.5 mm are fixed variables for the three cutting speeds that are varied. The cutting process uses a dry turning process with ASTM A 29 medium steel material. The results show the cutting process with Vc = 70 m / min, the cutting time (tc) 6.82 minutes there was a significant increase in tool wear (Vb) which reached 0.04 mm at 0.8 minutes, then in the turning process there was no sudden wear before 6 minutes with large side wear (Vb) of 0.06 at 6.82 minutes. In cutting using Vc = 110 m / min, tc 8.22 minutes there was a significant increase in Vb which reached 0.05 mm at 0.46 minutes, then in the process of turning there was a sudden wear at 6 minutes with large side wear (Vb) 0.13 at 8.22 minutes. On cutting using Vc = 250 m / min, tc 8.22 minutes there was a significant increase in Vb which reached 0.06 mm at 0.24 minutes, then in the process of turning there was a sudden wear at 6 minutes with large side wear (Vb) 0.18 at 6.20 minutes.
Keywords
Full Text:
PDF (Bahasa Indonesia)References
Nakaminami, M., Tokuma, T., Moriwaki, T., dan Nakamoto, K. Optimal Structure Design Methodology for Compound Multiaxis Machine Tool- I- Analysis of Requirements and Specification. Paper Manufacturing Technology Departement. MORI SEIKI CO.LTD. 2007
Kalpakjian, S. dan Steven, R.S. Manufacturing Processes for Engineering Materials. New Jersey.Prentice Hall. 2001
Budiman, Hendri dan Richard. “Analisis Umur Dan Keausan Pahat Karbida Untuk Membubut Baja Paduan (ASSAB 760) Dengan Metoda Variale Speed Machining Test”. Jurnal Teknik Mesin Universitas Kristen Petra. vol 9 (1), pp31-39, 2007
Astakhov V P . Tribology of Metal Cutting. Elsevier, London. 2006
Armansyah Ginting, Keausan Pahat Pemotong Kerbida. Jurusan Teknik Mesin Universitas Sumatra Utara. 2004
ISO 3685 (1977) Second Edition 1993.
Rochim, Taufiq. Teori & Teknologi Proses Pemesinan. Higher Education Development Support Project. Jakarta. Mei 1993.
David A.S and John S.A, Metal Cutting Theory and Practice, Marcel Dekker Inc., 1997.
Nouari M. dan Ginting A., Wear Characteristics and Ferformance of Multi-layer CVD-Coated Alloyed Carbide Tool in Dry End Milling of Titanium Alloy. Surface Coating Technology. 200:5663-5676. 2006
Zhang., An Investigation of the Wear Mechanism for Carbida Tool in Face Milling the Ti-5Al-4.75Mo-4.75 V- 1Cr-1 Fe Alloy. Key Eng Mater 431- 432:547-550. 2010
S. Sunarto and S. Mawarni, “Pengaruh pemesinan laju tinggi keadaan kering terhadap pertumbuhan aus sisi (VB) pahat karbida berlapis (tialn/tin) pada pembubutan paduan aluminium 6061,” J. POLIMESIN, vol. 16, no. 2, pp. 51–56, 2018.
F. Sitorus, A. Ginting, and B. Wirjosentono, “Penyelidikan Karakteristik Lapisan Diamond Film Pahat Karbida Terhadap Pembebanan Mekanik Pada Pembubutan Kering,” J. Inotera, vol. 1, no. 1, pp. 32–45, 2016.
I. Butarbutar, “Optimasi Kondisi Pemotongan pada Pembubutan Baja AISI 4340 yang Dikeraskan Menggunakan Pahat Karbida PVD Berlapis AlTiN dengan Algoritma Genetika,” Universitas Sumatera Utara, 2018.
A. Suhendi and M. Yoto, “Pengaruh Kecepatan Spindle, Kedalaman Penyayatan, dan Variasi Campuran Cairan Pendingin Terhadap Keausan Pahat Insert Karbida pada Proses Pembubutan,” J. Tek. Mesin Dan Pembelajaran, vol. 2, no. 2, 2019.
Sandvik Coromant, Technical Information: Tool wear, 12 maret 2004. http://www2.coromant.sandvik.com/coromant/products/steelturning/pdf/.2003
DOI: https://doi.org/10.30811/jpl.v18i2.1230
Refbacks
- There are currently no refbacks.
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-BerbagiSerupa 4.0 Internasional.
Mailing Address:
Jl. Banda Aceh-Medan
Km. 280,3, Buketrata, Mesjid Punteut, Blang Mangat,
Kota Lhokseumawe, 24301
Propinsi Aceh,
Indonesia
Comments on this article
"PeterDem" (2024-03-14)
"WilliamAbise" (2024-03-14)
"WilliamAbise" (2024-03-14)
"JulioLeask" (2024-03-14)
"JulioLeask" (2024-03-14)
"WilliamAbise" (2024-03-14)
"PeterDem" (2024-03-14)
"JulioLeask" (2024-03-14)
"WilliamAbise" (2024-03-14)
"JulioLeask" (2024-03-14)
"Robertopisy" (2024-03-14)
"AnthonyAlown" (2024-03-19)
"Brianbam" (2024-03-19)
"DanielInedo" (2024-03-19)
"DanielInedo" (2024-03-19)
"Brianbam" (2024-03-19)
"DanielInedo" (2024-03-19)