Pengaruh variasi arus pengelasan GTAW terhadap sifat mekanik material St 37

Rirismaranggi S Rirismaranggi S, Syamsuar Syamsuar, Sumardi Sumardi

Abstract


In the joints process by using welding many stages must be considered to get optimal results, starting from the design stage to the processing stage. Stages of design that starts from the selection of welding types to the selection of the seam angle used. Whereas at the processing stage, the appropriate current strength will be chosen up to the working position. The purpose of this study was to determine the effect of welding currents on the mechanical strength of St 37 steel on GTAW welding. In this study the material used was St 37 and the protective gas used was argon gas and the current variation used was 70 A, 75 A and 80 A. After conducting the research, the welding of GTAW on the St 37 material with current variations affected the tensile strength values , violence and stretches that occur after welding. The results obtained are 80 A welding current has the highest tensile strength and hardness compared to 75 A and 70 A which has the lowest tensile strength and hardness, while the highest strain occurs at 80A current of 10.59%, followed by 75A current with a value of stretch which occurred by 8.6% and the lowest in the current 70 A is 2.96%.

Keywords: GTAW, welding current, tensile strength, hardness


Abstrak

Pada proses penyambungan dengan menggunakan pengelasan banyak tahapan yang harus diperhatikan untuk mendapatkan hasil yang optimal, mulai dari tahapan desain sampai tahapan pengerjaan. Tahapan desain yang dimulai dari pemilihan jenis pengelasan sampai pada pemilihan sudut kampuh yang digunakan. Sedangkan pada tahapan pengerjaan akan dipilih kuat arus yang sesuai sampai pada posisi pengerjaan. Tujuan penelitian ini adalah untuk mengetahui pengaruh arus pengelasan terhadap kekuatan mekanik baja St 37 pada pengelasan GTAW. Pada penelitian ini material yang digunakan adalah St 37 dan gas pelindung yang digunakan adalah gas argon serta variasi arus yang digunakan adalah 70 A, 75 A dan 80 A. Setelah dilakukan penelitian, maka pengelasan GTAW pada material St 37 dengan variasi arus mempengaruhi nilai kekuatan tarik, kekerasan dan rengangan yang terjadi setelah pengelasan. Hasil yang didapat adalah arus pengelasan 80 A memiliki kekuatan tarik dan kekerasan yang tertinggi dibandingkan dengan 75 A dan 70 A yang memiliki kekuatan tarik dan kekerasan terendah, sedangkan rengangan yang tertinggi terjadi pada arus 80A sebesar 10.59%, selanjutnya diikuti oleh arus 75A dengan nilai rengangan yang terjadi sebesar 8.6% dan yang terendah pada arus 70 A yaitus sebesar 2.96%.

 

Kata kunci :  GTAW, arus pengelasan, kekuatan tarik, kekerasan


Full Text:

PDF

References


A. Q. M Yogi Nasrul L., Heru Suryanto, “PENGARUH VARIASI ARUS LAS SMAW TERHADAP KEKERASAN DAN KEKUATAN TARIK SAMBUNGAN DISSIMILAR STAINLESS STEEL 304 DAN ST 37,” J. Tek. Mesin, vol. 24, no. 01, pp. 1–12, 2016.

A. Azwinur, S. A. Jalil, and A. Husna, “PENGARUH VARIASI ARUS PENGELASAN TERHADAP SIFAT MEKANIK PADA PROSES PENGELASAN SMAW,” J. POLIMESIN, vol. 15, no. 2, p. 36, Sep. 2017.

S. A.Jalil, Z. Zulkifli, and T. Rahayu, “ANALISA KEKUATAN IMPAK PADA PENYAMBUNGAN PENGELASAN SMAW MATERIAL ASSAB 705 DENGAN VARIASI ARUS PENGELASAN,” J. POLIMESIN, vol. 15, no. 2, p. 58, Sep. 2017.

A. Supandi, “Pengujian Kekuatan Mekanik Hasil Sambungan Las Aluminium 5083 Dengan Metode Las Gtaw (Gas Tungsten Arc Welding),” Apr. 2019.

L. Andewi, “PENGARUH VARIASI ARUS PADA HASIL PENGELASAN TIG (TUNGSTEN INERT GAS) TERHADAP SIFAT FISIS DAN MEKANIS PADA ALUMUNIUM 6061,” 2016.

D. M. Sari, Pengaruh Suhu Preheating Pada Hasil Pengelasan Gtaw Terhadap Sifat Fisis Dan Mekanis Stainless Steel 304. 2015.

D. M. Sari, Pengaruh Suhu Preheating Pada Hasil Pengelasan Gtaw Terhadap Sifat Fisis Dan Mekanis Stainless Steel 304. 2015.

M. F. Kumayasari And A. I. Sultoni, “Studi Uji Kekerasan Rockwell Superficial Vs Micro Vickers Comparation Study Of Hardness Testing By Using Rockwell Superficial Vs Microvickers,” Vol. 2, No. 2, Pp. 85–89, 2017.

E. Saputra, “Pengaruh Arus Pengelasan Smaw Terhadap Sifat Mekanik Pada Material St 37,” Politeknik Negeri Lhokseumawe, 2012.


Refbacks

  • There are currently no refbacks.